DX53D+Z Galvanized Steel Sheet

Product Description

DX53D+Z Galvanized Steel Plate is a cold-rolled steel coated with a layer of zinc through hot-dip galvanization, offering excellent corrosion resistance and durability. It provides good formability and strength, making it suitable for applications in construction, automotive, home appliances, and manufacturing. Common uses include roofing, panels, automotive body parts, and components for household appliances. The zinc coating protects the steel from rust, extending its service life even in harsh environments. DX53D+Z combines high strength with good ductility, making it easy to process through bending, welding, and forming. Cost-effective and reliable, this steel is ideal for products that require both aesthetic appeal and long-term protection against corrosion.

DX53D+Z Galvanized Steel Sheet Standard Specification

Thickness	0.12~2.5mm
Width	1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc
Length	1000-6000 or Since the custom
Surface	Normal (uneven) spangle/ Skinpassed spangle/ Regular spangle / Minimized spangles
Form	Coils, Foils, Rolls, Plain coil, Shim coil, Perforated coil, Chequered coil, Strip, Flats, Blank (Circle), Ring (Flange) etc.

DX53D+Z Galvanized Steel Sheet Equivalent Material

Grade	Euronorm	China GB	Japanese JIS	US ASTM
Grade	EN 10346:2009	GBT 2518-2008	JIS:G3302-2005	ASTM A653M
DX53D+Z	DX53D+Z	DX53D+Z	SGCD2	FS TypeA FS TypeB

DX53D+Z Galvanized Steel Sheet Metal Content

Grade	Element	C	Si	Mn	P	S	Ti
DX53D+Z	Min.	-	-	-	-	-	-
DX53D+Z	Max.	0.12	0.5	0.6	0.12	0.045	0.3

Tensile strength: 270~380MPa
Yield strength: 140~260MPa
Elongation: ≥30%

Delong Warehouse

Product Inspection

The appearance of the coating is bright, meticulous, without sagging or wrinkles. Thickness inspection can use coating thickness gauge, the method is relatively simple. The thickness of the coating can also be obtained by converting the amount of zinc adhesion. For the bonding strength, a bending press can be used to bend the sample at 90-180°, and there should be no cracks or peeling of the coating. A heavy hammer can also be used to test, and the salt spray test and copper sulfate corrosion test can be done in batches.