DX52D+Z Galvanized Steel Sheet

Product Description

DX52D+Z Galvanized Steel Plate is a low-carbon steel coated with zinc through the hot-dip galvanization process, providing excellent corrosion resistance and durability. It offers good formability, making it ideal for applications requiring bending, stamping, and welding. The steel is commonly used in construction (e.g., roofing, panels), automotive (e.g., body panels, frames), and home appliances (e.g., refrigerators, washing machines). The zinc coating protects the steel from rust, extending its lifespan, while its strength and ductility ensure reliable performance in various environments. Cost-effective and versatile, DX52D+Z is widely used in industries where long-lasting, corrosion-resistant materials are crucial.

DX52D+Z Galvanized Steel Sheet Standard Specification

Thickness	0.12~2.5mm
Width	1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc
Length	1000-6000 or Since the custom
Surface	Normal (uneven) spangle/ Skinpassed spangle/ Regular spangle / Minimized spangles
Form	Coils, Foils, Rolls, Plain coil, Shim coil, Perforated coil, Chequered coil, Strip, Flats, Blank (Circle), Ring (Flange) etc.

DX52D+Z Galvanized Steel Sheet Equivalent Material

Grade	Euronorm	China GB	Japanese JIS	US ASTM
Grade	EN 10346:2009	GBT 2518-2008	JIS:G3302-2005	ASTM A653M
DX52D+Z	DX52D+Z	DX52D+Z	SGCD1	CS TypeC CS TypeB

DX52D+Z Galvanized Steel Sheet Metal Content

Grade	Element	C	Si	Mn	P	S	Ti
DX52D+Z	Min.	-	-	-	-	-	-
DX52D+Z	Max.	0.12	0.5	0.6	0.12	0.045	0.3

Tensile strength: 270~420MPa
Yield strength: 140~300MPa
Elongation: ≥26%

Delong Warehouse

Product Inspection

The appearance of the coating is bright, meticulous, without sagging or wrinkles. Thickness inspection can use coating thickness gauge, the method is relatively simple. The thickness of the coating can also be obtained by converting the amount of zinc adhesion. For the bonding strength, a bending press can be used to bend the sample at 90-180°, and there should be no cracks or peeling of the coating. A heavy hammer can also be used to test, and the salt spray test and copper sulfate corrosion test can be done in batches.